Product Details
【Characteristic】
☆ Compatibility is wide (soluble with hydroxyl acrylic acid, polyester, etc., thermosetting acrylic resin);
☆ Excellent gloss and fullness;
☆ High solid content, good leveling;☆ Good weather resistance.
☆ Excellent dry
【Use】
Incorporated into hydroxy acrylic resin, thermosetting acrylic resin, alkyd resin for gloss and fullness.
【Nature】
Component |
Imported polyol, polyacid copolymer |
Exterior |
Clear and transparent |
Viscosity 20-25pa.s/25℃ |
Acid value |
2-5mgKOH/g |
|
Solvent |
Xylene |
Color |
≤1(Fe-Co) |
Solid |
80±2% |
Hydroxyl value |
140 |
【Phase solubility and solubility】
KN588 |
+ |
KN582-5 |
+ |
Xylene |
+ |
Ethylene glycol monoethyl ether |
+ |
CAB551-0.2 |
+ |
KN7034P |
+ |
Trimethylbenzene |
+ |
Ethylene glycol monoethyl ether acetate |
+ |
|
+ |
|
+ |
Butyl acetate |
+ |
Isobutanol |
+ |
|
+ |
|
+ |
CYC |
+ |
n-butyl alcohol |
+ |
Note:+ =soluble in/phase soluble in ○=partial soluble/phase soluble —=nonsoluble/incompetence
【Reference formula】
Car finish paint |
Diluent |
||
KN6532P |
68 |
Xylene |
50 |
KN3885P |
10-15 |
CAC |
5 |
Xylene |
9 |
Butyl acetate |
25 |
Butyl ester |
5.8 |
PMA |
20 |
PMA |
7 |
|
|
EFKA3772 |
0.2 |
|
|
3390curing agent |
Proper amount |
|
|
|
|
Construction ratio:Main agent: curing agent: diluent=100:24.9:80-100
【Process condition】
☆Roasted conditions:self-drying
☆substrate:tinplate(polish)
【Inspection technical index】
Inspection item |
Detection method |
Reference standard |
Inspection standard |
Inspection result |
Gloss |
60 degrees |
GB/T9754-88 |
≥98 |
100 |
Hardness |
Pencil scratch |
GB/T6739-96 |
≥H |
1H |
Adhesive force |
Hundred Grid Method |
GB/T9286-98 |
100% |
100% |
Impact |
Impact method |
GB/T1732-93 |
≥50Kg.cm |
50cm(20μm) |
Flexibility |
Bending method |
GB/T1731-93 |
≤2mm |
1mm |
【storability】
☆ Keep away from heat and fire. Store in a cool, ventilated place. Keep the container tight.
☆ The warranty period of this product is 12 months from the date of production
【Packing specification】 barrel
【safety】
This product contains solvents, must be handled carefully, avoid contact with skin and eyes, other information please refer to material safety