【Characteristic】
☆ Hardness
☆ Low temperature curing
☆ Excellent salt spray resistance
☆ Good adhesion to electroplating substrate
【Use】
Non-ferrous metal, plating varnish, low temperature glass paint
【Nature】
|
Component |
Acrylic copolymer |
Exterior |
Clear and transparent |
Viscosity |
4.0-6.0pa.s/25℃ |
Acid value |
50-65mgKOH/g |
|
Solvent |
Xylene/Isobutanol |
Color |
≤1(Fe-Co) |
Solid |
60±2% |
|
|
【Phase solubility and solubility】
|
KN588 |
+ |
KN582-5 |
+ |
Xylene |
+ |
Ethylene glycol monoethyl ether |
+ |
|
E-44 |
+ |
|
+ |
Trimethylbenzene |
+ |
Ethylene glycol monoethyl ether acetate |
+ |
|
325 |
+ |
|
+ |
Butyl acetate |
+ |
Isobutanol |
+ |
|
303 |
+ |
|
+ |
CYC |
+ |
n-butyl alcohol |
+ |
Note:+ =soluble in/phase soluble in ○=partial soluble/phase soluble —=nonsoluble/incompetence
【Reference formula】
|
Electrogilding oil |
Diluent |
||
|
KN6042T |
45 |
Xylene |
45 |
|
KN582-5 |
18 |
Methylbenzene |
10 |
|
E-44 |
5 |
Butyl acetate |
15 |
|
n-butyl alcohol |
5 |
Isobutanol |
15 |
|
Adhesion agent |
2 |
DAA |
10 |
|
Diluent |
24．5 |
Ethylene glycol monoethyl ether |
5 |
|
Flatting agent |
0.5 |
|
|
【Process condition】
☆ Roasted conditions: 120℃×15min,test the corrosion resistance index after 24 hours
☆ substrate:tinplate（polish）
【Inspection technical index】
|
Inspection item |
Detection method |
Reference standard |
Inspection standard |
Inspection result |
|
Hardness |
Pencil scratch |
GB/T6739-96 |
≥2H |
2H |
|
Adhesive force |
Hundred Grid Method |
GB/T9286-98 |
100% |
100% |
|
Impact |
Impact method |
GB/T1732-93 |
≥30Kg.cm |
50cm(18μm) |
|
Flexibility |
Bending method |
GB/T1731-93 |
≤2mm |
1mm |
|
Nitric acid resistance |
Drop method |
----------------- |
No discoloration, no foaming |
55S |